钢纤维的直径或等效直径合格率不得低于90%，可采取重量法检验，每批次抽检100根，用天平称量，卡尺测其长度，要求得到的等效平均值满足规定。
原材料的检验：
必须满足上述原材料的质量控制标准，应按照公路工程施工技术规范的要求进行检验。
钢纤维混凝土的检验：
应重点检验钢纤维混凝土的和易性、塌落度和水灰比等，同The qualified rate of steel fiber diameter or equivalent diameter shall not be less than 90%. Weight method can be adopted for inspection. 100 pieces of steel fiber can be sampled for each batch, weighed by balance and measured by caliper. The required equivalent average value meets the requirements.
Inspection of raw materials:
It must meet the quality control standards of the above raw materials, and shall be inspected in accordance with the requirements of the technical specifications for highway engineering construction.
Inspection of steel fiber reinforced concrete:
The workability, slump, water cement ratio, etc. of steel fiber concrete shall be mainly inspected. Meanwhile, the distribution of steel fiber in concrete shall be inspected visually on site. The mixing time shall be prolonged if steel fiber agglomeration is found.时必须现场目检钢纤维在混凝土的分布情况，发现有钢纤维结团现象应延长拌和时间。

钢纤维混凝土弯拉强度设计值fftm=ftm（1+αtm?ρf?lf/df)；
其中，fftm，ftm－－钢纤维混凝土弯拉强度标准值，设计值；
αtm－－钢纤维对钢纤维混凝土抗拉强度影响系数，宜通过试验确定；
ρf－－钢纤维体积率（即钢纤维掺量体积率）；
lf－－钢纤维长度；
df－－钢纤维直径或等效直径；
lf/df－－钢纤维长径比。
钢纤维混凝土用于公路路面、机场道面、或其它采用弯拉强度为设计指标的结构时，与钢纤维混凝土相应的集体混凝土的弯拉强度设计值的分级和使用范围，可按国家现行有关水泥混凝土路面、机场道面等行业设计规范的规定采用。

钢纤维主要用于制造钢纤维混凝土，任何方法生产的钢纤维都能起到强化混凝土的作用。
纤维的增强效果主要取决于基体强度（fm），纤维的长径比（钢纤维长度l与直径d的比值，即I/d），纤维的体积率（钢纤维混凝土中钢纤维所占体积百分数），纤维与基体间的粘结强度（τ），以及纤维在基体中的分布和取向（η）的影响。当钢纤维混凝土破坏时，大都是纤维被拔出而不是被拉断，因此改善纤维与基体间的粘结强度是改善纤维增强效果的主要控制因素之一。
加入钢纤维的混凝土其抗压强度、拉伸强度、抗弯强度、冲击强度、韧性、冲击韧性等性能均得到较大提高。

钢纤维的直径或等效直径合格率不得低于90%，可采取重量法检验，每批次抽检100根，用天平称量，卡尺测其长度，要求得到的等效平均值满足规定。
原材料的检验：
必须满足上述原材料的质量控制标准，应按照公路工程施工技术规范的要求进行检验。
钢纤维混凝土的检验：
应重点检验钢纤维混凝土的和易性、塌落度和水灰比等，同时必须现场目检钢纤维在混凝土的分布情况，发现有钢纤维结团现象应延长拌和时间。